A self cured bis-acryl auto-mix system with low viscosity, composed of Ethoxylated, Bis-gma multifunctional methacrylate esters, glass filler and nanofiller for a simple alternative to traditional materials. Prime-Crown™ produces minimal odor, shrinkage and heat generation. Good wear resistance for better translucency. Obtaining a smooth surface for esthetic appearance and protection against staining with satisfactory working time.
High polish. High compressive strength
Seven popular vita shades: A1, A2, A3, A3.5, B1, B2, Bleach
Low shrinkage. Low heat generation
Compressing strength: 340 MPa
Transverse strength: 76 MPa
Vickers hardness: 25 MPa
Linear polymerization shrinkage: 18%
Radiopaque: Yes
Prime-Dent® Copal Varnish & Solvent Insulates against thermal and electric shock. Provides a strong bond between dentin and restoration. Chloroform free formula of varnish and sealant.
A composite based core material designed for the easy fabrication of core build-ups. The core material is a dual cure, fluoride releasing resin core material. Dispensed with an applicator gun and auto mixed in mixing...
This cement has a sedative effect on the pulp and is especially useful for cementation on prepared teeth with exposed dentinal tubules. The addition of polymers as reinforcing agents have transformed it into a final...
Cementation of crowns, bridges and splints. Retention of temporary crowns, sealing dressing in teeth during root canal therapy procedures. Trial cementation of permanent restorations prior to final insertion. Testing of interproximal contact prior to final...